Method of treating manganese and iron manganese lean ore, there are three: First, mechanical processing, including washing, calcination, re-election, high intensity magnetic separation, flotation, roasting, etc.; Second Fire beneficiation, Hyperphosphate HSR When the refractory ore is used, the method of pyrometallurgical ore dressing is also called the manganese-rich slag method. The third is chemical beneficiation. When the quality requirements of the product components are very pure, and the above methods cannot meet the requirements, chemical purification is adopted. (chemical beneficiation) approach.
The high manganese slag method is a pyrometallurgical method. It is a high-iron high-phosphorus refractory manganese ore that cannot be directly used for smelting. It is selectively reduced in a blast furnace or an electric furnace to ensure sufficient reduction of elements such as iron and phosphorus. Under the premise, the reduction of manganese is suppressed, thereby obtaining a manganese-rich slag having a high manganese and low phosphorus and a large m(Mn)/m(Fe) ratio. This is a method of enriching manganese ore in line with China's situation. Because China's manganese-rich ore is rare, high-iron and high-phosphorus-selected manganese ore accounts for more than 40% of China's manganese ore reserves. Manganese-rich slag in China has been vigorously developing countries, providing high-quality raw materials for the production of iron alloy.
Fire method beneficiation has the following advantages compared with mechanical beneficiation.
(1) The sorting effect is good, and it can deal with various types of manganese ore, especially for the high-iron high-phosphorus manganese ore with complex structure containing phosphorus and finely dip-dyed, and ferromanganese cemented. It is difficult to obtain good indicators by mechanical selection. The manganese-rich slag method works well (see Table 1).

Table 1 Â Compare Agate Hill manganese ore index
project		Main ingredients (%)			m(Mn)	m(P)	Manganese recovery rate /%
project		Mn	Fe	P	m(Fe)	m(Mn)	Manganese recovery rate /%
Mechanical beneficiation	Manganese oxide ore	17.23	27.00	0.039	0.637	0.0026	ã€€
Mechanical beneficiation	Roasting magnetic separation	27.13	11.52	0.038	2.35	0.0014	63.91
Pyrolysis	Manganese oxide ore	17.51	41.20	0.02	0.424	0.0015	ã€€
Pyrolysis	Manganese-rich residue	39.88	2.70	0.008	14.80	0.0002	85.00

(2) The product quality is good, mainly containing high manganese, high manganese-iron mass ratio and low phosphorus content.
(3) Manganese recovery is high, reaching 85%~90%, which is 5% higher than mechanical beneficiation (see Table 2).

Table 2 Â Quality index of smelting manganese-rich slag in blast furnace
Factory Name	Main ingredients (%)			m(Mn)	m(P)	Manganese recovery rate /%
Factory Name	Mn	Fe	P	m(Fe)	m(Mn)	Manganese recovery rate /%
Shanghai Iron and Steel Factory	35~42	1 to 2	0.05	13~38	0.0015	81ï½ž90
Xiangtan Manganese Mine	37.7	2.03.0	0.05	12.4	0.0013	82ï½ž88
Yingkou Ferroalloy Factory	35~37	1.5	0.005	24.1	0.0002	90
Agate Mountain Mine	39~40	2.7	0.008	14.8	0.0002	85
Dao County Refining Plant	36~40	1.5 to 3.0	0.008	13~24	0.0002	80ï½ž85
Donghuqiao Manganese Mine	38~42	1.0 to 2.0	0.03	21~38	0.0007	80ï½ž85
Huangyang Sizhi Refinery	40ï½ž45	1.5 to 3.0	0.025	15~27	0.0006	80ï½ž85

(4) The product has good physical properties, high manganese slag strength, and is not affected by environmental influences for long-term storage and long-distance transportation.
The shortcoming of high manganese slag production is that smelting consumes a lot of coke and electricity, the production cost is slightly higher, the smelting process can only remove iron and phosphorus and other non-ferrous metals, can not remove gangue, and because coke is brought into ash, it also makes The amount of impurities increases.
The main uses of manganese-rich slag are as follows:
(1) It is used as a raw material for the production of manganese-silicon alloy. When smelting manganese-silicon alloy in electric furnace, the ratio of manganese-rich slag is generally 30%~40%, and the purpose is to adjust m(Mn)/m(Fe) of manganese raw material into the furnace. And m(P)/m(Mn). Since manganese-rich slag contains high SiO ₂ , it is mainly used to produce manganese-silicon alloy.
The production of high silicon manganese silicon alloy, because the manganese content in the manganese-containing raw materials is required to be greater than 40%, iron is less than 1%, and phosphorus is less than 0.03%, almost all of the manganese-rich slag can be used to smelt qualified products.
(2) For the production of manganese metal by fire method, when manganese metal is produced by electrothermal method, all manganese-rich slag is used (w(Mn)>40%, w(Fe)<1%, w(P)< 0.03%) is used as a raw material, and a high silicon manganese alloy is used as a reducing agent.
(3) Ingredients for the production of electric furnace ferromanganese and medium and low carbon ferromanganese.
(4) Ingredients for smelting blast furnace ferromanganese. (3) In item (4), m(Mn)/m(Fe) and m(P)/m(Mn) are mainly transferred to the furnace raw materials to ensure that the product quality meets the requirements.

Air Humidifier

What is a air humidifier?

Essential Oil humidifier therapy adds moisture to the air to prevent dryness that can cause irritation in many parts of the body. Cool mist humidifiers can be particularly effective for treating dryness of the skin, nose, throat, and lips. They can also ease some of the symptoms caused by the flu or common cold.

What can I use a mist humidifier for?

Humidity acts as a natural moisturizing agent that can relieve dryness. For this reason, home humidifiers are often used for relieving:

dry skin
sinus congestion/headache
dry throat
nose irritation
bloody noses
irritated vocal cords
dry cough
cracked lips

You may be prone to these discomforts when the air in your home is dry. This is especially common during winter months or when an air conditioner is being used during the summer.

Essential Oil Humidifier,Air Humidifier,Mist Humidifier,Cool Mist Humidifier

Shenzhen Dituo Electronic Co.,Ltd. , https://www.sz-dituo.com